1, Xy104 high temperature enamel repair agent can be used alone or as substrate.
Xy406 high-temperature enamel repair agent is used for fabric
2, Xy104 high temperature enamel repair agent can withstand 200 ºC.
3, It can resist general inorganic acid, organic acid, alcohol, alkali, amine, etc.
For example: 10% hydrochloric acid, 10% nitric acid, carbonic acid, 10% hydrobromic acid, 20% nitrite, 5% phosphoric acid, 10% sulfuric acid, 20% ammonia water, lime water, 20% potassium hydroxide, 20% sodium hydroxide, propanol, butanol, ethylene glycol, diethyl hydrogen salt, methylamine (water content 75%), bicarbonate, mineral oil, inorganic salt, etc.
4, Weight: 1000g, origin: USA
5, When the load is 1kg, the data are as follows: H10 wheel (wet) 572cm3 / CS17 wheel per thousand revolution (dry)
23cm3 / 1000 rpm
6, According to ASTM d1002, the adhesive force tensile shear (surface sandblasting treatment) of 1 mm medium carbon steel was as follows: natural curing 148kg / cm2, heating curing (100 ºC) 134kg / cm2, heating curing (180 ºC) 116kg / cm2
7, According to ASTM d695, the compressive strength is 1122kg / cm2 natural curing, 1790kg / cm2 heating curing (100 ºC);
1560kg / cm2 heat curing (180 ºC)
8, According to ASTM D256, the impact strength is 36j / M natural curing 37.5j/m heating curing (100 ºC) 43j / M heating curing (180 ºC)
9, According to ASTM D648, the thermal denaturation temperature is: 58 ºC natural curing; 136 ºC heating curing (100 ºC); 220 ºC heating curing (180 ºC)
10, Ratio: weight mixing ratio 4:1, volume ratio 3:1
Storage period: from 0 ºC to 30 ºC, separate storage for at least 5 years.
Scope of application: repair all kinds of mechanical wear surface, container porcelain surface, scratches, pits, cracks, etc. Such as: shaft, bearing bush, hydraulic parts, machine tool guide rail, steel body, pump, valve, reactor / tank, condenser, etc.
Xy406 high-temperature enamel repair agent is used for fabric
2, Xy104 high temperature enamel repair agent can withstand 200 ºC.
3, It can resist general inorganic acid, organic acid, alcohol, alkali, amine, etc.
For example: 10% hydrochloric acid, 10% nitric acid, carbonic acid, 10% hydrobromic acid, 20% nitrite, 5% phosphoric acid, 10% sulfuric acid, 20% ammonia water, lime water, 20% potassium hydroxide, 20% sodium hydroxide, propanol, butanol, ethylene glycol, diethyl hydrogen salt, methylamine (water content 75%), bicarbonate, mineral oil, inorganic salt, etc.
4, Weight: 1000g, origin: USA
5, When the load is 1kg, the data are as follows: H10 wheel (wet) 572cm3 / CS17 wheel per thousand revolution (dry)
23cm3 / 1000 rpm
6, According to ASTM d1002, the adhesive force tensile shear (surface sandblasting treatment) of 1 mm medium carbon steel was as follows: natural curing 148kg / cm2, heating curing (100 ºC) 134kg / cm2, heating curing (180 ºC) 116kg / cm2
7, According to ASTM d695, the compressive strength is 1122kg / cm2 natural curing, 1790kg / cm2 heating curing (100 ºC);
1560kg / cm2 heat curing (180 ºC)
8, According to ASTM D256, the impact strength is 36j / M natural curing 37.5j/m heating curing (100 ºC) 43j / M heating curing (180 ºC)
9, According to ASTM D648, the thermal denaturation temperature is: 58 ºC natural curing; 136 ºC heating curing (100 ºC); 220 ºC heating curing (180 ºC)
10, Ratio: weight mixing ratio 4:1, volume ratio 3:1
Storage period: from 0 ºC to 30 ºC, separate storage for at least 5 years.
Scope of application: repair all kinds of mechanical wear surface, container porcelain surface, scratches, pits, cracks, etc. Such as: shaft, bearing bush, hydraulic parts, machine tool guide rail, steel body, pump, valve, reactor / tank, condenser, etc.