1, Syl-d20 glass enamel repair agent is suitable for glass lined reaction tank / kettle to repair enamel dropping, iron exposure, perforation, etc.
This repair agent belongs to the base material, can be used alone, each group weighs 1 kg.
 
2, Syl-d20 glass lining repair agent, with a maximum temperature resistance of 130 degrees.
 
3, Basic parameters
Appearance and volume after mixing
The volume of the base material is 412 cm3 after mixing with 1kg deep lime mud
Curing time of curing agent and plaster
The mixing ratio (base material: curing agent) is shown in the table below
When the weight mixing ratio is 5:1, the storage period is 0 ºC - 30 ºC, the storage period is at least 5 years
The volume mixing ratio is 3:1

4, The mediums suitable for glass lining reaction tank (kettle) of syl-d20 are: generally resistant to inorganic acids, organic acids, alcohols, alkalis, amines & amides, beverages & foods, alcohols & ethers, gases, halocarbons, mineral oils, vegetable / animal oils, salts, hydrocarbons, etc. Such as: carbonic acid, 10% hydrochloric acid, 20% nitric acid, propylene glycol, citric acid, ethylene glycol, propylene glycol, 2-methoxyethanol, calcium hydroxide, 10% potassium hydroxide, di (III) ethanolamine, ethyl acetate, methylamine (water 75%), lime water, dibutyl phthalate, isopropyl ether, etc.
 
5, Operation and curing time of syl-d20 repairing agent for glass lining
Temperature: 5 ºC 10 ºC 15 ºC 20 ºC 25 ºC 30 ºC

The operation time limit is 35 minutes, 25 minutes and 15 minutes

Handling or use: 4 hours 3 hours 2 hours 15 minutes 1 hour 45 minutes 1 hour 45 minutes
Machining or light load: 6 hours - 4 hours - 3 hours - 2 hours - 1 hour 30 minutes - 1 hour
Full mechanical or thermal load: 4 days - 2 days - 1.5 days - 20 hours - 16 hours
Soak in chemicals for 5 days, 4 days, 3 days, 2 days, 1 and a half days